In Materials Science , fatigue is the progressive and localised structural damage that occurs when a material is subjected to cyclic or fluctuating Strains at nominal Stresses that cause structural failure. The maximum values are often significantly less than the Ultimate Tensile Stress , and may be below the Yield Stress of the material. CHARACTERISTICS OF FATIGUE FAILURES
TIMELINE OF EARLY FATIGUE HISTORY
HIGH-CYCLE FATIGUE Historically, most attention has focused on situations that require more than 104 cycles to failure where stress is low and deformation primarily Elastic . The S-N curve In high-cycle fatigue situations, materials performance is commonly characterised by an ''S-N curve'', also known as a ''Wöhler curve''. This is a graph of the magnitude of a cyclical stress (''S'') against the Logarithmic Scale of cycles to failure (''N''). S-N curves are derived from tests on samples of the material to be characterised (often called ''coupons'') where a regular Sinusoid al stress is applied by a testing machine which also counts the number of cycles to failure. This process is sometimes known as ''coupon testing''. Each coupon test generates a point on the plot though in some cases there is a ''runout'' where the time to failure exceeds that available for the test (see Censoring ). Analysis of fatigue data requires techniques from Statistics , especially survival analysis and Linear Regression . Probabilistic nature of fatigue As coupons sampled from a homogeneous frame will manifest variation in their number of cycles to failure, the S-N curve should more properly be an ''S-N-P curve'' capturing the probability of failure after a given number of cycles of a certain stress. Probability distributions that are common in data analysis and in design against fatigue include the Lognormal Distribution , Extreme Value Distribution and Weibull Distribution . Complex loadings In practice, a mechanical part is exposed to a complex, often Random , sequence of loads, large and small. In order to assess the safe life of such a part: #Reduce the complex loading to a series of simple cyclic loadings using a technique such as Rainflow Analysis ; #Create an Histogram of cyclic stress from the rainflow analysis; #For each stress level, calculate the degree of cumulative damage incurred from the S-N curve; and #Combine the individual contributions using an algorithm such as ''Miner's rule''. Miner's rule In 1945 , M. A. Miner popularised a rule that had first been proposed by A. Palmgren in 1924 . The rule, variously called ''Miner's rule'' or the ''Palmgren-Miner linear damage hypothesis'', states that where there are ''k'' different stress magnitudes in a spectrum, ''Si'' (1 ≤ ''i'' ≤ ''k''), each contributing ''ni''(''Si'') cycles, then if ''Ni''(''Si'') is the number of cycles to failure of a constant stress reversal ''Si'', failure occurs when: : C is experimentally found to be between 0.7 and 2.2. Usually for design purposes, C is assumed to be 1. This can be thought of as assessing what proportion of life is consumed by stress reversal at each magnitude then forming a linear combination of their aggregate. Though Miner's rule is a useful approximation in many circumstances, it has two major limitations: #It fails to recognise the probabilistic nature of fatigue and there is no simple way to relate life predicted by the rule with the characteristics of a probability distribution. #There is sometimes an effect in the order in which the reversals occur. In some circumstances, cycles of high stress followed by low stress cause more damage than would be predicted by the rule. Paris' Relationship Paris derived relationships for the stage II crack growth with cycles N, in terms of the cyclical component ΔK of the Stress Intensity Factor K where 2a is the crack length and m is typically in the range 3 to 5. This relationship was later modified (by Forman, 1967 {Link without Title} ) to make better allowance for the mean stress, by introducing a factor depending on (1-R) where R = min. stress/max stress, in the denominator.. LOW-CYCLE FATIGUE Where the stress is high enough for Plastic Deformation to occur, the account in terms of stress is less useful and the Strain in the material offers a simpler description. Low-cycle fatigue is usually characterised by the ''Coffin-Manson relation'' (published independently by L. F. Coffin in 1954 and S. S. Manson 1953 ): : -where:
FATIGUE AND FRACTURE MECHANICS The account above is purely phenomenological and, though it allows life prediction and design assurance, it does not enable life improvement or design optimisation. For the latter purposes, an exposition of the causes and processes of fatigue is necessary. Such an explanation is given by fracture mechanics in four stages. #Crack nucleation; #Stage I crack-growth; #Stage II crack-growth; and #Ultimate ductile failure. FACTORS THAT AFFECT FATIGUE-LIFE Magnitude of stress including stress concentrations caused by part geometry. Quality of the surface; surface roughness, scratches, etc. cause stress concentrations or provide crack nucleation sites which can lower fatigue life depending on how the stress is applied. On the other hand, surface stress can be intentionally manipulated to increase fatigue life. For example, Shot Peening is widely used to put the surface in a state of compressive stress which inhibits surface crack formation and thus improves fatigue life. Such techniques for producing surface stress are often referred to generically as '' Peening '', whatever the mechanism used to produce the stress. Other more recently introduced surface treatments, such as Laser Peening and Ultrasonic Impact Treatment , can also produce this surface compressive stress and can increase the fatigue life of the component. This improvement is normally observed only for high-cycle fatigue. Little improvement is obtained in the low-cycle fatigue régime. Material Type. Certain materials, such as steel, will never fail due to fatigue if the stresses remain below a certain level. Other materials, such as aluminum, will eventually fail due to fatigue regardless of the stresses the material sees. Surface defect geometry and location. The size, shape, and location of surface defects such as scratches, gouges, and dents can have a significant impact on fatigue life. Significantly uneven cooling, leading to a heterogeneous distribution of material properties such as hardness and ductility and, in the case of alloys, structural composition. Uneven cooling of castings, for example, can produce high levels of tensile Residual Stress , which will encourage crack growth. Size, frequency, and location of internal defects. Casting defects such as gas porosity and shrinkage voids, for example, can significantly impact fatigue life. In metals where strain-rate sensitivity is observed (ferrous metals, copper, titanium, etc.) strain rate also affects fatigue life in low-cycle fatigue situations. For non-isotropic materials, the direction of the applied stress can affect fatigue life. Grain size; for most metals, fine-grained parts exhibit a longer fatigue life than coarse-grained parts. Environmental conditions and exposure time can cause erosion, corrosion, or gas-phase embrittlement, which all affect fatigue life. Corrosion Fatigue is a problem encountered in many aggressive environments. The operating temperature over which the part is exposed to affects fatigue life. DESIGN AGAINST FATIGUE Dependable design against fatigue-failure requires thorough education and supervised experience in Structural Engineering , Mechanical Engineering , or Materials Science . There are three principal approaches to life assurance for mechanical parts that display increasing degrees of sophistication: #Design to keep stress below threshold of fatigue limit (infinite lifetime concept); #Design (conservatively) for a fixed life after which the user is instructed to replace the part with a new one (a so-called ''lifed'' part, finite lifetime concept, or "safe-life" design practice); #Instruct the user to inspect the part periodically for cracks and to replace the part once a crack exceeds a critical length. This approach usually uses the technologies of Nondestructive Testing and requires an Accurate prediction of the rate of crack-growth between inspections. This is often referred to as damage tolerant design or "retirement-for-cause". Stopping fatigue Fatigue cracks that have begun to propagate can sometimes be stopped by regarding metal fatigue damage to the Manahawkin Bay Bridge in New Jersey However, it is not recommended because a hole represents a Stress Concentration factor of about 2. There is thus the possibility of a new crack starting in the side of the hole. It is always far better to replace the cracked part entirely. Several disasters have been caused by botched repairs to cracked structures, such as JAL 123 . Material change Changes in the materials used in parts can also improve fatigue life. Parts can be made from better fatigue rated metals for example. Complete replacement and redesign of parts can also reduce if not eliminate fatigue problems. Thus Helicopter Rotor blades and Propellor s in metal are being replaced by Composite equivalents. They are not only lighter, but also much more resistant to fatigue. They are more expensive, but the extra cost is amply repaid by their greater integrity, since loss of a rotor blade usually leads to total loss of the aircraft. A similar argument has been made for replacement of metal fuselages, wings and tails of aircraft. INFAMOUS FATIGUE FAILURES Versailles Train Crash On May 8 , 1842 one of the trains carrying revellers on their return from Versailles to Paris , having witnessed the celebrations of the birthday of Louis Philippe , derailed and caught Fire . Though the resulting conflagration mutilated the dead beyond recognition or enumeration, it is estimated that 53 perished and around 40 were seriously injured. The derailment had been the result of a broken Locomotive axle. Rankine's investigation of broken axles in Britain highlighted the importance of Stress Concentration , and the mechanism of crack growth with repeated loading. De Havilland Comet Metal fatigue came strongly to the notice of aircraft engineers in 1954 after three De Havilland Comet passenger jets had broken up in mid-air and crashed within a single year. Investigators from the Royal Aircraft Establishment at Farnborough in England told a public enquiry that the Sharp Corners around the plane's window openings (actually the forward ADF antenna window in the roof) acted as initiation sites for cracks. The skin of the aircraft was also too thin, and cracks from manufacturing stresses were present at the corners. All aircraft windows were immediately redesigned with rounded corners. Others